- 4 Grinding. If the design calls for flat ends on the spring, the ends are ground at this stage of the manufacturing process. The spring is mounted in a jig to ensure the correct orientation during grinding, and it is held against a rotating abrasive wheel until the desired degree of flatness is obtained. When highly automated equipment is used, the spring is held in a sleeve while both ends are ground simultaneously, first by coarse wheels and then by finer wheels. An appropriate fluid (water or an oil-based substance) may be used to cool the spring, lubricate the grinding wheel, and carry away particles during the grinding.
- 5 Shot peening. This process strengthens the steel to resist metal fatigue and cracking during its lifetime of repeated flexings. The entire surface of the spring is exposed to a barrage of tiny steel balls that hammer it smooth and compress the steel that lies just below the surface.
- 6 Setting. To permanently fix the desired length and pitch of the spring, it is fully compressed so that all the coils touch each other. Some manufacturers repeat this process several times.
7 Coating. To prevent corrosion, the entire surface of the spring is protected by painting it, dipping it in liquid rubber, or plating it with another metal such as zinc or chromium. One process, called mechanical plating, involves tumbling the spring in a container with metallic powder, water, accelerant chemicals, and tiny glass beads that pound the metallic powder onto the spring surface.
Alternatively, in electroplating, the spring is immersed in an electrically conductive liquid that will corrode the plating metal but not the spring. A negative electrical charge is applied to the spring. Also immersed in the liquid is a supply of the plating metal, and it is given a positive electrical charge. As the plating metal dissolves in the liquid, it releases positively charged molecules that are attracted to the negatively charged spring, where they bond chemically. Electroplating makes carbon steel springs brittle, so shortly after plating (less than four hours) they must be baked at 325-375F (160-190C) for four hours to counteract the embrittlement.
- 8 Packaging. Desired quantities of springs may simply be bulk packaged in boxes or plastic bags. However, other forms of packaging have been developed to minimize damage or tangling of springs. For example, they may be individually bagged, strung onto wires or rods, enclosed in tubes, or affixed to sticky paper.